Method for manufacturing semiconductor device having element isolation structure

ABSTRACT

When a semiconductor device having an element isolation structure is formed, first, a trench is formed in a wafer from a principal surface of the wafer, and the trench is filled with an insulating film. Then, the back surface of the wafer is polished so that the insulating film is exposed on the back surface. Accordingly, the insulating film penetrates the wafer from the principal surface to the back surface, thereby performing element isolation of the wafer. It is not necessary to use a bonding wafer. Thus, the method for manufacturing the semiconductor device is simplified.

CROSS REFERENCE TO RELATED APPLICATION

[0001] This application is a Continuation-in-part Application of U.S. application Ser. No. 09/708,046, filed on Nov. 8, 2000. The present invention is based upon and claims the benefit of Japanese Patent Application No. 11-326930 filed on Nov. 17, 1999, the contents of which are incorporated herein by reference.

BACKGROUND OF THE INVENTION

[0002] 1. Field of the Invention

[0003] This invention relates to a method for manufacturing a semiconductor device adopting an element isolation structure.

[0004] 2. Description of the Related Art

[0005] An SOI (Silicon On Insulator) structure is conventionally known as an element isolation structure. FIGS. 4A to 4F show a process for manufacturing a semiconductor device in which element isolation is achieved by an SOI structure, and the method for manufacturing this semiconductor device is explained below.

[0006] First, as shown in FIG. 4A, oxide films 13 a, 13 b are respectively formed, by surface oxidation, on a support wafer 11 and a wafer 12 for element formation (element formation wafer) each of which is composed of a silicon wafer. After that, the surfaces of the oxide films 13 a, 13 b are bonded together, and accordingly, an SOI substrate shown in FIG. 4B is formed, in which the support wafer 11 and the element formation wafer 12 are bonded together with an oxide film 13 interposed between them.

[0007] Successively, as shown in FIG. 4C, the element formation wafer 12 is mechanically polished until the thickness of the element formation wafer 12 falls in a range of several μm to about 20 μm, and mirror finishing is performed. Then, as shown in FIG. 4D, trenches 14 are formed such that the trenches 14 extend from the surface of the element formation wafer 12 to the oxide film 13. Element isolation is performed by filling the trenches 14 with an oxide film or poly silicon.

[0008] After that, elements (not shown) are formed in respective regions that are isolated from one another, and as shown in FIG. 4E, the SOI substrate is divided into chips. Then, as shown in FIG. 4F, for example, a chip is die-mounted on a substrate 17 such as a metallic plate through conductive paste 16. Thus, a semiconductor device to which element isolation is performed by the SOI structure is finished. In this constitution, however, because the bonding wafer having the support wafer 11 is necessitated, the cost is high due to causes such as that the processing number is increased.

SUMMARY OF THE INVENTION

[0009] The present invention has been made in view of the above problems. An object of the present invention is to simplify a method for manufacturing a semiconductor device having an element isolation structure.

[0010] According to the present invention, briefly, after a trench is formed in a wafer from a principal surface of the wafer, the trench is filled with an insulating film. Then, the thickness of the wafer is thinned from a back surface of the wafer so that the insulating film is exposed on the back surface. Accordingly, element isolation of the wafer can be achieved by the insulating film penetrating the wafer from the principal surface to the back surface. It is not necessary to use a bonding wafer. As a result, the method for manufacturing the semiconductor device can be simplified.

BRIEF DESCRIPTION OF THE DRAWINGS

[0011] Other objects and features of the present invention will become more readily apparent from a better understanding of the preferred embodiment described below with reference to the following drawings, in which;

[0012]FIGS. 1A to 1E are cross-sectional views showing a process for manufacturing a semiconductor device adopting an element isolation structure according to a preferred embodiment of the present invention;

[0013]FIGS. 2A to 2F are cross-sectional views showing a process for manufacturing a semiconductor device adopting an element isolation structure according to a preferred embodiment of the present invention.

[0014]FIGS. 3A to 3B are cross-sectional views showing a part of process for manufacturing a semiconductor device adopting an element isolation structure according to a preferred embodiment of the present invention; and

[0015]FIGS. 4A to 4F are cross-sectional views showing a process for manufacturing a semiconductor device adopting a conventional SOI structure.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

[0016] A method for manufacturing a semiconductor device adopting an element isolation structure according to the preferred embodiment is explained with reference to FIGS. 1A to 1E.

[0017] First, as shown in FIG. 1A, an element formation wafer 1 composed of a silicon substrate is prepared. For example, the wafer 1 may be a so-called epi-wafer in which an n⁺ type embedded layer and an n⁻ type epitaxial growth layer are provided on a p⁻ type substrate, but it can be appropriately selected in accordance with a semiconductor element that is formed. Then, as shown in FIG. 1B, trenches 2 are formed in the wafer 1 from a principal surface 1 a of the wafer 1 at a specific depth (for example, several μm to about 20 μm), and insides of the trenches 2 are filled up with an insulating film 3 such as an oxide film or poly silicon. Accordingly, adjacent two of several element formation regions 4 of the wafer 1 are isolated by the insulating film 3 provided therebetween. Successively, although it is not shown, desired elements are formed in the respective element formation regions 4 isolated from one another, and a wiring layer, a surface protective film, and the like are formed.

[0018] Next, as shown in FIG. 1C, the other surface (back surface) 1 b of the wafer 1 is polished by a CMP (Chemical Mechanical Polish) until the insulating film 3 is exposed. For example, when the depth of the trenches is 20 μm, the wafer 1 is thinned so that its thickness becomes about 15 μm. After that, as shown in FIG. 1D, the wafer 1 is divided into chips by dicing. Then, as shown in FIG. 1E, each chip is die-mounted on a mounting board 6 such as a metallic plate through insulating paste (insulating adhesive) 5. Thus, the semiconductor device adopting an element isolation structure is completed.

[0019] According to the method described above, a bonding wafer that is used in a conventional SOI structure is not necessitated. The element isolation structure can be provided by performing the element formation step to the one wafer 1. Because of this, the element isolation structure can be simplified, and the manufacturing process of the semiconductor device to which the element isolation structure is adopted can be simplified simultaneously. As a result, cost reduction can be attained.

[0020] Also in the case of the conventional SOI structure, to take an electrical potential of a support wafer, the support wafer is die-mounted on a metallic plate or the like through conductive paste. To the contrary, in the case of the present embodiment, because such support wafer is not used and it is not necessary to take the electrical potential, the chip can be die-mounted by the insulating paste 5. This also contributes to cost reduction.

[0021] In the above-mentioned embodiment, although the back surface 1 b is polished by the CMP method, it may be thinned by other methods such as etching. Besides in the above-mentioned embodiment, although the chip and the mounting board 6 are bonded together by the insulating adhesive 5 so that the insulating isolation at the chip back surface is provided, the insulating isolation may be attained by forming an insulating film such as an oxide film on the chip back surface. For example, in the step shown in FIG. 1C, after the back surface 1 b of the wafer 1 is polished, an oxide film can be formed on the back surface by oxidizing the back surface of the wafer 1.

[0022] Next, more specific method for thinning a wafer will be described with reference to FIGS. 2A to 3B.

[0023] Similarly to the embodiment described above, an element formation wafer 21 composed of silicon substrate is prepared. This wafer also has a structure to form semiconductor elements such as a bi-polar transistor, a MOS transistor, or the like. In FIG. 3A, a bi-polar transistor 24 a and a MOS transistor 24 b are formed at a principal surface of the wafer. Wirings composed of polycrystalline silicon or aluminum, an interlayer oxide film, passivation film, or the like are formed on the principal surface of the wafer, although these are not shown in the drawings. Trenches 23 are formed in the wafer from the principal surface 21 a. The trenches 23 do not reach a back surface 21 b of the wafer 21. Moreover, the trenches 23 are formed deeper than a thickness of the wafer after polishing is performed, which is described in greater detail below.

[0024] Then, the wafer 21 is thinned to a predetermined thickness using a CMP (Chemical mechanical Polishing) apparatus. The predetermined thickness is thinner than a thickness corresponding to a depth of the trenches 23, for example, several μm to several ten μm.

[0025] More specifically, as shown in FIG. 2B, the wafer 21 is fixed to a holder 30 with a wax 32 so that a side of the principal surface is attached to the holder 30. The holder 30 has a guide ring 31 to regulate a polishing thickness of the wafer 21. The guide ring 31 has a thickness t so as to control the thickness of the wafer that is to be left. The thickness t of the guide ring is in a range from several μm to several ten μm. Incidentally, when the guide ring is not formed in the holder 30, the thickness of the wafer may be measured optically, for example, by using a laser apparatus. That is, the thickness of the wafer is checked by measurement with the laser apparatus while the polishing of the wafer is performed.

[0026] The wafer attached to the holder 30 is pressed to a polishing stage (polishing pad) 40 and is rotated with respect to the polishing stage 40. Moreover, the polishing stage is also rotated. Slurry including abrasives is supplied on the polishing stage 40 by a dispenser 50 to polish the wafer. When the guide ring 31 contacts the polishing stage 40, the polishing is finished. The guide ring 31 is composed of a hard metal such as Molybdenum. Therefore, the guide ring 31 is not polished so that the polishing is finished.

[0027] Then, an oxide film (not shown) is formed at the back surface of the wafer that is exposed after the polishing is finished, so that the MOS transistor 24 b is insulated from the bi-polar transistor 24 a with the trench 23 and the oxide film.

[0028] After that, the wafer is separated into chips by dicing with a dicing blade 60.

[0029] Finally, semiconductor devices without respective supporting substrates are formed through the above-mentioned process. The supporting wafer is unnecessary since the supporting substrates are unnecessary for the devices, so that cost for producing the semiconductor devices can be cut down.

[0030] Incidentally, disadvantage may occur due to thinness of the wafer or the devices when the thinned wafer is handled or diced. In this case, a supporting substrate 25 can be attached to the back surface of the wafer with adhesive such as a paste including silver after the polishing is finished as shown in FIG. 3A. The supporting substrate may be composed of a metal such as cupper. The thinned wafer 21 can be detached from the holder 30 and transferred with the supporting substrate. Moreover, the thinned wafer 21 is separated into chips with the supporting substrate by using the dicing blade 60 as shown in FIG. 3B. In this case, the supporting substrate 25 works as a heat sink or a pedestal.

[0031] While the present invention has been shown and described with reference to the foregoing preferred embodiment, it will be apparent to those skilled in the art that changes in form and detail may be made therein without departing from the scope of the invention as defined in the appended claims. 

What is claimed is:
 1. A method for manufacturing a semiconductor device, comprising: preparing a wafer having a principal surface and a back surface; forming a trench in the wafer from the principal surface, the trench dividing a surface portion of the wafer into first and second element formation regions; filling the trench with an insulating layer; forming a first and second elements in the first and second element formation regions, respectively; and thinning a thickness of the wafer from the back surface without attaching a supporting substrate thereto so as to expose the insulating layer at the back surface after the first and second elements are formed.
 2. The method according to claim 1, further comprising: dicing the wafer into a plurality of chips after the thickness of the wafer is thinned; and mounting one of the plurality of chips on a mounting substrate.
 3. The method according to claim 2, wherein the one of the plurality of chips is mounted on the mounting substrate through an insulating adhesive.
 4. The method according to claim 1, further comprising, after the thickness of the wafer is thinned, forming a back surface insulating film on the back surface of the wafer.
 5. The method according to claim 1, wherein the thickness of the wafer is thinned by chemical mechanical polishing.
 6. The method according to claim 1, further comprising, after the thickness of the wafer is thinned, attaching a substrate on the back surface of the wafer.
 7. A method for manufacturing a semiconductor device, comprising: preparing a wafer having a principal surface and a back surface; forming a trench in the wafer from the principal surface; filling the trench with an insulating layer; forming semiconductor elements in respective regions isolated from each other with the trench in the wafer; thinning a thickness of the wafer from the back surface without attaching a supporting substrate thereto so that the insulating layer filling the trench is exposed on both the principal surface and the back surface of the wafer after the semiconductor elements are formed; and cutting a cutting portion of the wafer other than a region where the trench is formed to divide the wafer into a plurality of chips.
 8. The method according to claim 7, further comprising, after the thickness of the wafer is thinned and before the wafer is cut, attaching a substrate on the back surface of the wafer. 